Aluminium Alloy - ASTM & FED-QQ - QQ-A-225/6 T351 Bar

QQ-A-225/6 T351 Bar

A medium to high strength alloy with, dependent upon temper, minimum Proof Stress up to 58 ksi / 400 Mpa and minimum Tensile Strength up to 66 ksi / 455 MPa

Chemical Composition

Spec: SAE AMS QQ-A-225/6

Alloy QQ A 225/6

Chemical Element % Present
Silicon (Si) 0.0 - 0.50
Iron (Fe) 0.0 - 0.50
Copper (Cu) 3.80 - 4.90
Manganese (Mn) 0.30 - 0.90
Chromium (Cr) 0.0 - 0.10
Magnesium (Mg) 1.20 - 1.80
Zinc (Zn) 0.0 - 0.25
Titanium (Ti) 0.0 - 0.15
Titanium + Zirconium (Ti+Zr) 0.0 - 0.20
Other (Each) 0.0 - 0.05
Others (Total) 0.0 - 0.15
Aluminium (Al) Balance


Physical PropertyValue
Density 2.79 g/cm³
Melting Point 640 °C
Thermal Expansion 23.1 x10^-6 /K
Modulus of Elasticity 73 GPa
Thermal Conductivity 121-150 W/m.K
Electrical Resistivity 30-40 % IACS
'Typical' Physical Properties are given

Spec: SAE AMS QQ-A-225/6

Bar - 12.7mm to 165.1mm

Mechanical PropertyValue
Proof Stress 310 MIN MPa
Tensile Strength 427 Min MPa
Elongation A50 mm 10 Min %

Alloy Designations

Aluminium alloy QQ-A-225/6 has similarities to the following standard designations and specifications but may not be a direct equivalent:

AMS 4120, Alloy 2024, UNS A92024

Temper Types

Alloy QQ-A-200/3 is supplied in a wide range of tempers:

  • O - Soft
  • T42 - Solution heat treated and naturaly aged to a substantially stable condition
  • T8510 - Solution heat treated, stress-relieved by stretching then artificially aged
  • T8511 - Solution heat treated, stress-relieved by stretching then artificially aged
  • T4 - Solution heat treated and naturally aged to a substantially stable condition
  • T6 - Solution heat treated and artificially aged
  • T62 - Solution heat treated then artificially aged by the user
  • T351 - Solution heat treated then stress relieved by stretching. Equivalent to T4 condition.
  • T36 - Solution heat treated then cold worked by a reduction of 6%
  • T851 - Solution heat treated then stress relieved by stretching then artificially aged.

Supplied Forms

Alloy QQ-A-200/3 is supplied in Bar, Rod and Wire

  • Bar
Download PDF Version

Datasheet Search

Last Datasheet Revision

18 July 2019


This Data is indicative only and as such is not to be relied upon in place of the full specification. In particular, mechanical property requirements vary widely with temper, product and product dimensions. All information is based on our present knowledge and is given in good faith. No liability will be accepted by the Company in respect of any action taken by any third party in reliance thereon.

Please note that the 'Datasheet Update' date shown above is no guarantee of accuracy or whether the datasheet is up to date.

The information provided in this datasheet has been drawn from various recognised sources, including EN Standards, recognised industry references (printed & online) and manufacturers’ data. No guarantee is given that the information is from the latest issue of those sources or about the accuracy of those sources.

Material supplied by the Company may vary significantly from this data, but will conform to all relevant and applicable standards.

As the products detailed may be used for a wide variety of purposes and as the Company has no control over their use; the Company specifically excludes all conditions or warranties expressed or implied by statute or otherwise as to dimensions, properties and/or fitness for any particular purpose, whether expressed or implied.

Advice given by the Company to any third party is given for that party’s assistance only and without liability on the part of the Company. All transactions are subject to the Company’s current Conditions of Sale. The extent of the Company’s liabilities to any customer is clearly set out in those Conditions; a copy of which is available on request.